2mm NM340 NM500 Steel Plate Cold Rolled 600mm-3500mm Width Wear Steel Plate

Characteristics
WearTuf 500 is a fully martensitic Q&T abrasion resistant steel having a hardness of average 450 Brinell. WearTuf 500 combines wear resistant properties with excellent weldability and bending performance. Due to the high impact toughness, WearTuf 500 offers very good crack integrity.

Dimensions
WearTuf 500 is supplied in the thickness rage of 4.0 - 50.0 mm and in the plate width of 900 – 3 100 mm. Supplied plate length from 4 000 to 18 000 mm.

Impact toughness
Typical 35J/-40°C (-40°F)
The impact toughness is given as absorbed energy at temperature, being the average of three full size Charpy-V test samples in longitudinal direction to rolling, according to EN ISO 148-1.

Hardness guarantee
Surface hardness: 470-530 Brinell
Guaranteed hardness range, measured on a milled surface at a depth of 0.5 – 2.0 mm below the plate surface, according to ISO EN 6506-1.
Min center hardness:
Plate thickness ≤ 20mm: min 470 Brinell
Plate thickness ＞ 20mm: 95% of min guaranteed surface hardness.

Applications
WearTuf 500 is mainly uesd within the mining and recycling industry. Common applications are: heavy dumper and tipper bodies, buckets, cutting edges, hammers, shredders, crushers, sieves and various lining parts.

Ultrasonic testing
All plates delivered meets the Class E2, S2 requirement, according to EN 10160.

Delivery condition
WearTuf 500 is delivered in the as quenched (Q) condition, and when found necessary in the condition of quenched and tempered (QT).
The plates are delivered with sheared or thermally cut edges.

Tolerances
The thickness tolerances of WearTuf 500 meets and exceeds the thickness tolerance of EN 10029 Class A . Tolerances on shape, length, and width meets the requirements of EN 10029. Flatness tolerances conforms to EN 10 029 Class S or closer.


Surface condition and properties
The delivered surface finish meets and exceeds that of EN 10163-2 Class A, Subclass 3.
The plates will be delivered as painted, using a low zinc silicate corrosion protective shop primer. Plates can also be delivered as unpainted.

Heat Treatment
Since the properties in the as delivery condition cannot be retained after exposure at service temperatures above 250°C, WearTuf 500 is not intended for further heat treatment.

Chemical Composition
Ladle analysis: The steel is grain refined and fully killed, wt% CEV = C + Mn/6 + (Cr + Mo + V)/5 + (Ni + Cu)/15
CET = C + (Mn + Mo)/10 + (Cr + Cu)/20 + Ni/40

Mechanical Properties